现代化工  2022, Vol. 42 Issue (8): 70-74    DOI: 10.16606/j.cnki.issn0253-4320.2022.08.015
  技术进展 本期目录 | 过刊浏览 | 高级检索 |
碳基材料脱硝催化剂的研究进展
张超, 郝敏彤, 孙维, 冯彬, 朱丽娜
中国石油石油化工研究院大庆化工研究中心, 黑龙江 大庆 163714
Research progress on carbon-based materials for denitration catalysts
ZHANG Chao, HAO Min-tong, SUN Wei, FENG Bin, ZHU Li-na
Daqing Petrochemical Research Center, Petrochemical Research Institute, PetroChina Company Limited, Daqing 163714, China
下载:  PDF (2764KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 综述了近几年碳基材料在氨气选择性还原(NH3-SCR)技术上取得的相关研究成果,列举了以活性炭、活性炭纤维、碳纳米管、石墨烯为脱硝载体的负载型催化剂的研究现状,分析了烟气中的水和二氧化硫对SCR催化剂活性的影响,对碳基材料催化剂今后的发展方向做出展望。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
张超
郝敏彤
孙维
冯彬
朱丽娜
关键词:  碳基材料  NH3-SCR  脱硝  催化剂    
Abstract: This article summarizes the related research results about the application of carbon-based materials in ammonia selective reduction (NH3-SCR) technology in recent years,and reviews the supported catalysts with activated carbon,activated carbon fiber,carbon nanotubes,and graphene as denitration carriers.The influence of water and sulfur dioxide in flue gas on the activity of SCR catalyst is analyzed,and the development direction of carbon-based material supported catalyst in the future is prospected.
Key words:  carbon-based materials    NH3-SCR    denitration    catalyst
收稿日期:  2021-08-05      修回日期:  2022-06-23           出版日期:  2022-08-20
ZTFLH:  Q426.99  
通讯作者:  张超(1994-),男,硕士,助理工程师,研究方向为脱硝催化剂的制备,通讯联系人,963265634@qq.com。    E-mail:  963265634@qq.com
引用本文:    
张超, 郝敏彤, 孙维, 冯彬, 朱丽娜. 碳基材料脱硝催化剂的研究进展[J]. 现代化工, 2022, 42(8): 70-74.
ZHANG Chao, HAO Min-tong, SUN Wei, FENG Bin, ZHU Li-na. Research progress on carbon-based materials for denitration catalysts. Modern Chemical Industry, 2022, 42(8): 70-74.
链接本文:  
https://www.xdhg.com.cn/CN/10.16606/j.cnki.issn0253-4320.2022.08.015  或          https://www.xdhg.com.cn/CN/Y2022/V42/I8/70
[1] Xiong Z B,Li Z Z,Du Y P,et al.Starch bio-template synthesis of W-doped CeO2 for selective catalytic reduction of NO with NH3:Influence of ammonia titration[J].Journal of Physics and Chemistry of Solids,2020,148:109727.
[2] Chai Y X,Zhang G Z,He H,et al.Theoretical study of the catalytic activity and Anti-SO2 poisoning of a MoO3/V2O5 selective catalytic reduction catalyst[J].ACS Omega,2020,5(42):26978-26985.
[3] 王冬,王新频.低温NH3-SCR脱硝过渡金属基催化剂的研究进展[J].新世纪水泥导报,2020,26(4):1-10.
[4] Zhou G Y,Maitarad P,Wang P L,et al.Alkali-resistant NO<i>x reduction over SCR catalysts via boosting NH3 adsorption rates by in-situ constructing the sacrificed sites[J].Environmental Science&Technology,2020,54(20):13314-13321.
[5] Geng Y,Shan W P,Liu F D,et al.Adjustment of operation temperature window of Mn-Ce oxide catalyst for the selective catalytic reduction of NO<i>x with NH3[J].Journal of Hazardous Materials,2021,405:124223.
[6] Lázaro M J,Ascaso S,Pérez-Rodríguez S,et al.Carbon-based catalysts:Synthesis and applications[J].Comptes Rendus Chimie,2015,18(11):1229-1241.
[7] Peng K,Zhou J,Xu W,et al.Microwave irradiation-selective catalytic reduction of NO to N2 by activated carbon at low temperature[J].Energy&Fuels,2017,31(7):7344-7351.
[8] Chen J Y,Zhu B Z,Sun Y L,et al.Investigation of low-temperature selective catalytic reduction of NO<i>x with ammonia over Mn-modified Fe2O3/AC catalysts[J].Journal of the Brazilian Chemical Society,2018,29(1):79-87.
[9] Jiang L J,Liu Q C,Ran G J,et al.V2O5-modified Mn-Ce/AC catalyst with high SO2 tolerance for low-temperature NH3-SCR of NO[J].Chemical Engineering Journal,2019,370:810-821.
[10] Shu Y,Zhang F,Wang H C.Manganese-cerium mixed oxides supported on rice husk based activated carbon with high sulfur tolerance for low-temperature selective catalytic reduction of nitrogen oxides with ammonia[J].RSC Advances,2019,9(41):23964-23972.
[11] Wang M X,Liu H,Huang Z H,et al.Activated carbon fibers loaded with MnO2 for removing NO at room temperature[J].Chemical Engineering Journal,2014,256:101-106.
[12] 郑玉婴,徐哲,张延兵,等.Mn-Fe/ACF催化剂低温选择性催化还原NO[J].功能材料,2014,45(20):20142-20145.
[13] Lu P,Xing Y,Li C T,et al.A reusable material with high performance for removing NO at room temperature:Performance,mechanism and kinetics[J].Catalysis Science&Technology,2016,6(10):3520-3528.
[14] Jiang X,Lu P,Li C T,et al.Experimental study on a room temperature urea-SCR of NO over activated carbon fibre-supported CeO2-CuO[J].Environmental Technology,2013,34(5/6/7/8):591-598.
[15] Qu Z P,Miao L,Wang H,et al.Highly dispersed Fe2O3 on carbon nanotubes for low-temperature selective catalytic reduction of NO with NH3[J].Chemical Communications Royal Society of Chemistry,2015,51(5):956-958.
[16] 张延兵,李晓环,刘巧巧,等.Mn-FeO<i>x/PDOPA@CNTs催化剂的原位制备及低温脱硝性能[J].化学工程,2021,49(2):18-23.
[17] Valtanen A,Huuhtanen M,Rautio A R,et al.Noble metal/CNT based catalysts in NH3 and EtOH assisted SCR of NO[J].Topics in Catalysis,2015,58(14/15/16/17):984-992.
[18] Lv X,Zheng Y,Zhang L H,et al.low-temperature selective catalytic reduction of NO with NH3 over Mn-Fe mixed metal oxides on the nitric vapor functionalized carbon nanotubes prepared by a polyol process[J].Nano Brief Reports and Reviews,2017,12(4):1750048.
[19] Ren B N.The preparation of Mn-Fe/CNTs catalyst at the low-temperature selective catalytic reduction of NO with NH3[J].Journal of Materials Science and Chemical Engineering,2018,6(12):33-38.
[20] Guo Z Y,Wang M X,Huang Z H,et al.Preparation of graphene/carbon hybrid nanofibers and their performance for NO oxidation[J].Carbon,2015,87:282-291.
[21] 焦金珍,李时卉,黄碧纯.石墨烯负载MnO<i>x催化剂的制备及其低温NH3-SCR活性[J].物理化学学报,2015,31(7):1383-1390.
[22] 王光应,刘江峰,徐辉.一种高负载Ru-MnO<i>x/石墨烯脱硝催化剂的制备方法:CN105413674A[P].2016-03-23.
[23] You X C,Sheng Z Y,Yu D Q,et al.Influence of Mn/Ce ratio on the physicochemical properties and catalytic performance of graphene supported MnO<i>x-CeO2 oxides for NH3-SCR at low temperature[J].Applied Surface Science,2017,423:845-854.
[24] 李鹏,李智芳,耿翠,等.Mo掺杂Ce/石墨烯(GE)催化剂的制备及脱硝性能[J].无机化学学报,2018,34(12):88-93.
[25] Geng C,Li Z F,Cui J X,et al.Low-temperature NO reduction performance of peanut shell-derived few-layer graphene loaded CeCo<i>xMn1-xO3 catalyst[J].Journal of Dispersion Science and Technology,2020,42(6):1-10.
[26] Kang Y,Li Z F,Cui J X,et al.Addition of Ce in Cu/three-dimensional graphene derived from watermelon for low temperature NH3-SCR[J].Chemistry Select,2020,5(4):1364-1369.
[27] Lu X N,Song C Y,Jia S H,et al.Low-temperature selective catalytic reduction of NO<i>x with NH3 over cerium and manganese oxides supported on TiO2-graphene[J].Chemical Engineering Journal,2015,260:776-784.
[28] Xiao X,Sheng Z Y,Yang L,et al.Low-temperature selective catalytic reduction of NO<i>x with NH3 over a manganese and cerium oxide/graphene composite prepared by a hydrothermal method[J].Catalysis Science&Technology,2016,6(5):1507-1514.
[29] Deng J L,Liu J X,Song W Y,et al.Selective catalytic reduction of NO with NH3 over Mo-Fe/beta catalysts:The effect of Mo loading amounts[J].RSC Advances,2017,7(12):7130-7139.
[30] Bai S L,Zhao J H,Wang L,et al.SO2-promoted reduction of NO with NH3 over vanadium molecularly anchored on the surface of carbon nanotubes[J].Catalysis Today,2010,158(3/4):393-400.
[1] 陈亚莉, 袁铭霞, 朱贤, 晏金灿, 薛原, 韩生. 多相纳米催化剂制备生物柴油的研究进展[J]. 现代化工, 2022, 42(8): 22-26.
[2] 宋青明, 许蓉, 李闯, 李军峰, 杨红军, 陈建. 连续流微反应器快速合成邻甲基环己基醋酸酯的研究[J]. 现代化工, 2022, 42(8): 96-99.
[3] 沈蒙莎, 程永兵, 黄鸿坤, 徐雨, 樊俊杰, 徐文媛, 陈曦, 廖梦垠. NaAlCl4/γ-Al2O3@ZSM-5空心微球核壳复盐催化剂的制备及歧化性能研究[J]. 现代化工, 2022, 42(8): 100-104112.
[4] 王淼, 余钊卓, 刘香君, 徐芙清, 王俊淇. 石墨烯基材料在生物质催化转化中的应用[J]. 现代化工, 2022, 42(7): 46-50.
[5] 耿新国, 杨卫亚, 隋宝宽, 王刚. 碳基载体石油馏分加氢脱硫催化剂研究进展[J]. 现代化工, 2022, 42(7): 75-78,83.
[6] 宋卫余, 杨坤, 赖自强, 宋少佳. Mo基、W基催化剂的制备及其丙烷脱氢性能研究[J]. 现代化工, 2022, 42(7): 120-124,129.
[7] 张蕊, 王思月, 洪耀华, 马星宇, 姜晓乐. 二维沸石咪唑骨架有效催化二氧化碳电还原的研究[J]. 现代化工, 2022, 42(7): 125-129.
[8] 田鑫, 李欣, 王薇, 吕鹏, 马保军. Co/Si/Mo/Ni/Al2O3催化剂对汽油加氢脱硫性能的影响[J]. 现代化工, 2022, 42(7): 130-134,140.
[9] 张以民, 刘洋, 陈侣, 张雄志. 超分子水凝胶原位制备纳米镍及其在对硝基苯酚催化还原中的应用[J]. 现代化工, 2022, 42(6): 124-128,134.
[10] 杨美如, 吕岩, 马立超, 丁传敏, 王俊文. 过氧化氢存在下甲烷低温转化的研究进展[J]. 现代化工, 2022, 42(5): 19-23.
[11] 袁梦明, 唐焯林, 李冰晶, 李涛, 朱华丽, 陈召勇. 聚吡咯基碳纳米管的制备及在锂二氧化碳电池中的应用研究[J]. 现代化工, 2022, 42(5): 92-96.
[12] 唐兆吉, 杜艳泽, 姜艳, 陈阳. 镍源对含硫前体加氢裂化催化剂反应性能的影响[J]. 现代化工, 2022, 42(5): 97-101,108.
[13] 闫蕊, 刘志琪, 任浩, 吕凤圆, 吴明雄, 张建鹏, 李亚雯, 王凯. 碳纳米管负载NiCo催化剂的制备及析氧性能研究[J]. 现代化工, 2022, 42(5): 188-191,196.
[14] 魏佳伦, 于丽梅, 闫磊, 高占先. 用于双酚芴合成的离子液体催化剂的制备[J]. 现代化工, 2022, 42(5): 206-211.
[15] 许明阳, 包生伟, 林德溪, 马方圆. 连续重整在线更换高密度催化剂的研究[J]. 现代化工, 2022, 42(5): 239-242.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-37
版权所有 © 《现代化工》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn