Abstract: A simple two-step hydrothermal method and annealing process are used to prepare heterostructured Co3O4@CoMoO4 arrays on nickel foam.Thanks to its 3D heterostructure and synergy effect,Co3O4@CoMoO4 has a higher specific surface area and better electrocatalytic oxygen evolution performance than Co3O4/NF.The as-prepared Co3O4@CoMoO4/NF presents excellent oxygen evolution stability,achieving a low overpotential of 253 mV at 50 mA cm-2 with a Tafel slope of 64 mV dec-1 in 1 M KOH solution.Therefore it has good application prospects as catalysts for oxygen evolution reaction.
孙志裕, 黄小琴, 刘国强. 异质结构Co3O4@CoMoO4阵列的制备与析氧性能研究[J]. 现代化工, 2021, 41(3): 202-206,210.
SUN Zhi-yu, HUANG Xiao-qin, LIU Guo-qiang. Preparation of heterostructured Co3O4@CoMoO4 arrays and their oxygen evolution property. Modern Chemical Industry, 2021, 41(3): 202-206,210.
[1] Shi Q,Zhu C,Du D,et al.Robust noble metal-based electrocatalysts for oxygen evolution reaction[J].Chemical Society Reviews,2019,48:3181-3192. [2] Suen N T,Hung S F,Quan Q,et al.Electrocatalysis for the oxygen evolution reaction:Recent development and future perspectives[J].Chem Soc Rev,2017,46(2):337-365. [3] Chandrasekaran S,Yao L,Deng L,et al.Recent advances in metal sulfides:From controlled fabrication to electrocatalytic,photocatalytic and photoelectrochemical water splitting and beyond[J].Chemical Society Reviews,2019.48:4178-4280. [4] Huang L,Zhang W,Xiang J,et al.Hierarchical core-shell NiCo2O4@NiMoO4 nanowires grown on carbon cloth as integrated electrode for high-performance supercapacitors[J].Scientific Reports,2016,6:31465. [5] Xu Y,Kraft M,Xu R,et al.Metal-free carbonaceous electrocatalysts and photocatalysts for water splitting[J].Chemical Society Reviews,2016,45:3039-3052. [6] Wang X W,Zheng D L,Yang P Z,et al.Preparation and electrochemical properties of NiO-Co3O4 composite as electrode materials for supercapacitors[J].Chemical Physics Letters,2016,667:260-266. [7] Nai J,Lu Y,Yu L,et al.Formation of Ni-Fe mixed diselenide nanocages as a superior oxygen evolution electrocatalyst[J].Advanced Materials,2017,29:1703870. [8] Zhong D Z,Zhang L,Li C C,et al.Nanostructured NiFe (Oxy)hydroxide with easily oxidized Ni towards efficient oxygen evolution reaction[J].Journal of Materials Chemistry A,2018,6(38):16810-16817. [9] Chen Z,Zhao B,He Y C,et al.NiCo2O4 nanoframes with a nanosheet surface as efficient electrocatalysts for the oxygen evolution reaction[J].Materials Chemistry Frontiers,2018,2:1155-1164. [10] Conway B E,Liu T C,et al.Comparative behaviour of the kinetically significant surface intermediate states in anodic O2 evolution at oxide electrocatalyst materials:Participation of mediator redox couples in the oxide[J].Materials Chemistry & Physics,1989,22(1-2):163-182. [11] Huang Z F,Wang J,Peng Y,et al.Design of efficient bifunctional oxygen reduction/evolution electrocatalyst:Recent advances and perspectives[J].Advanced Energy Materials,2017,7(23):1700544. [12] Peng H,Jing C,Chen J,et al.Crystal structure of nickel manganese-layered double hydroxide@cobaltosic oxides on nickel foam towards high-performance supercapacitors[J].Cryst Eng Comm,2019,21(3):470-477. [13] 高文军.CoS2和CoP材料的合成及其催化析氧应用[J].现代化工,2019,39(10):134-137. [14] Wu F,Liao Q,Cao F,et al.Non-noble bimetallic NiMoO4,nanosheets integrated Si photoanodes for highly efficient and stable solar water splitting[J].Nano Energy,2017,34:8-14.