现代化工  2020, Vol. 40 Issue (12): 231-234    DOI: 10.16606/j.cnki.issn0253-4320.2020.12.049
  分析测试 本期目录 | 过刊浏览 | 高级检索 |
全固态新型铵离子选择性电极的制备及性能
刘斯洋1, 颜家保1, 夏正海2, 汪坤2, 李静1, 胡杰1, 赵振悦1, 贾彪1
1. 武汉科技大学化学与化工学院, 煤转化与新型炭材料湖北省重点实验室, 湖北 武汉 430081;
2. 中韩(武汉)石油化工有限公司, 湖北 武汉 430082
Preparation and properties of a novel all-solid-state ammonium ion selective electrode
LIU Si-yang1, YAN Jia-bao1, XIA Zheng-hai2, WANG Kun2, LI Jing1, HU Jie1, ZHAO Zhen-yue1, JIA biao1
1. Hubei Province Key Laboratory of Coal Conversion and New Carbon Materials, School of Chemistry and Chemical Engineering, Wuhan University of Science and Technology, Wuhan 430081, China;
2. SINOPEC-SK(Wuhan) Petrochemical Company Limited, Wuhan 430082, China
下载:  PDF (1511KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 采用循环伏安法,在玻碳电极上电沉积聚苯胺作为固态接触层,再将铵离子敏感膜溶液滴涂于固态接触层表面,制得了全固态新型铵离子选择性电极,并优化了固态接触层和敏感膜的制备工艺,提高了电极的性能。测试结果表明,该电极在10-1~10-5 mol/L范围内呈现能斯特响应,响应斜率为59.30 mV/dec,检测下限低至5.0×10-6 mol/L,重复测定的相对标准偏差小于2%;与商用电极相比,消除了Na+的干扰并提高了K+的选择性;用于实际废水分析时,电极检测结果准确、性能稳定,具有良好的应用前景。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
刘斯洋
颜家保
夏正海
汪坤
李静
胡杰
赵振悦
贾彪
关键词:  铵离子  离子选择性电极  全固态  聚苯胺    
Abstract: Polyaniline is electrodeposited onto a glassy carbon electrode as solid contact layer by cyclic voltammetry method,and a novel all-solid-state ammonium ion selective electrode is prepared by dripping ammonium ion sensing membrane solution on the surface of solid contact layer.The preparation technologies of solid contact layer and sensitive film are optimized to improve the performance of electrode.The test results show that this electrode exhibits Nernst response for ammonium ion with a slope of 59.30 mV·dec-1 over the concentration range of 10-1-10-5 mol·L-1,and the detection limit is as low as 5.0×10-6 mol·L-1.Relative standard deviation of the electrode repeatability is less than 2%.Compared with a commercial electrode,the prepared electrode can eliminate the interference of Na+ and improve the selectivity of K+.When it is used in the actual wastewater detection,the detection results are accurate and the performance of the electrode is stable,indicating a potential application prospect.
Key words:  ammonium ion    ion selective electrode    all-solid-state    polyaniline
收稿日期:  2020-01-16      修回日期:  2020-10-12          
ZTFLH:  X832  
基金资助: 湖北省科技创新专项重大项目(2017ACA179)
通讯作者:  颜家保(1964-),男,硕士,教授,研究方向为废水生物强化及深度处理研究,通讯联系人,972787445@qq.com。    E-mail:  972787445@qq.com
作者简介:  刘斯洋(1991-),男,硕士生,研究方向为电化学传感器
引用本文:    
刘斯洋, 颜家保, 夏正海, 汪坤, 李静, 胡杰, 赵振悦, 贾彪. 全固态新型铵离子选择性电极的制备及性能[J]. 现代化工, 2020, 40(12): 231-234.
LIU Si-yang, YAN Jia-bao, XIA Zheng-hai, WANG Kun, LI Jing, HU Jie, ZHAO Zhen-yue, JIA biao. Preparation and properties of a novel all-solid-state ammonium ion selective electrode. Modern Chemical Industry, 2020, 40(12): 231-234.
链接本文:  
https://www.xdhg.com.cn/CN/10.16606/j.cnki.issn0253-4320.2020.12.049  或          https://www.xdhg.com.cn/CN/Y2020/V40/I12/231
[1] 冀春苗,王晓爽,谢一多,等.离子选择性电极法测定污水处理厂进出水中的氨氮含量[J].净水技术,2017,(6):81-85.
[2] 顾金凤,凌芳,曹丽丽,等.水样中氨氮分析方法的研究[J].化学试剂,2015,37(5):420-424.
[3] Del Valle M,Gallardo J,De-Roman M,et al.An electronic tongue using potentiometric all-solid-state PVC-membrane sensors for the simultaneous quantification of ammonium and potassium ions in water[J].Analytical and Bioanalytical Chemistry,2003,377(2):248-256.
[4] Huang Y,Li J,Yin T,et al.A novel all-solid-state ammonium electrode with polyaniline and copolymer of aniline/2,5-dimethoxyaniline as transducers[J].Journal of Electroanalytical Chemistry,2015,741:87-92.
[5] 阚雅婷.基于邻苯二胺和18-冠醚-6新型全固态铵离子选择电极的研制与性能比较[D].杭州:浙江大学,2017.
[6] 安清波,贾菲,许佳楠,等.全固态离子选择性电极研究进展[J].中国科学:化学,2017,47(5):30-37.
[7] Bobacka J.Conducting polymer-based solid-state ion-selective electrodes[J].Electroanalysis,2006,18(1):7-18.
[8] Zahran E M,New A,Gavalas V,et al.Polymeric plasticizer extends the lifetime of PVC-membrane ion-selective electrodes[J].Analyst,2014,139:757-763.
[9] 李发闯,苏光,郭战永,等.电化学合成聚苯胺膜及其腐蚀防护性能[J].电镀与精饰,2019,41(10):5-8.
[10] 黄元凤.用于水体中部分营养盐原位探测的全固态电极的研制及表征[D].杭州:浙江大学,2017.
[1] 刘萍, 燕宇, 秦海利, 刘欢欢. 基于Co3O4/C复合水凝胶的全固态柔性超级电容器的研究[J]. 现代化工, 2020, 40(2): 89-94.
[2] 谢永刚, 陶萱, 陈方永, 王雪枫, 李娟娟, 高歌. 含氮多孔碳材料的制备及其对乙炔氢氯化反应催化性能研究[J]. 现代化工, 2020, 40(10): 155-159,164.
[3] 莫恒亮, 李锁定, 杨志涛, 唐阳, 万平玉, 陈咏梅, 孟晓冬. 高选择性铵离子筛α-MnO2-Na的制备及应用研究[J]. 现代化工, 2019, 39(6): 85-88,90.
[4] 王新海, 马珍珍. 电化学法制备的聚苯胺/石墨烯复合材料的微结构及性能研究[J]. 现代化工, 2019, 39(5): 156-159.
[5] 孙洁, 王黎明, 沈勇, 徐丽慧, 邱雨, 王沥莹. 铜钴镍铁氧体/聚苯胺复合物的制备及其性能研究[J]. 现代化工, 2019, 39(1): 105-109.
[6] 刘志森, 张志远, 徐鑫. 二氧化锰为氧化剂制备多孔石墨烯@聚苯胺超级电容器材料的研究[J]. 现代化工, 2017, 37(7): 117-120.
[7] 严祥辉, 蒙紫薇, 李维勇, 刘佳. 氮掺杂石墨烯用于碱性燃料电池产过氧化氢[J]. 现代化工, 2017, 37(5): 62-66.
[8] 徐泽杨, 毕淑娴, 詹海娟, 马宝军, 陈小燕, 刘万毅. HSO3-PAHAC固体酸催化大豆油酯交换合成生物柴油[J]. 现代化工, 2017, 37(11): 93-96,98.
[9] 邓子悦, 白盼星, 王师霞, 何永锋, 李论, 陈胜. 自分散聚苯胺/聚丙烯酸复合水性涂料的制备及其防腐蚀性能研究[J]. 现代化工, 2016, 36(3): 107-110.
[10] 吴之强, 詹海鹃, 马保军, 李冰, 刘万毅. 煤基碳基固体酸的制备及其催化合成环己酮甘油缩酮[J]. 现代化工, 2016, 36(11): 133-136,138.
[11] 刘贺峰, 赵东风, 李石, 杜聪聪, 王永强. PANI/Fe-N-TiO2复合材料的制备和光催化性能研究[J]. 现代化工, 2015, 35(3): 120-123.
[12] 曹慧, 高肖汉, 吕雪川, 伍家伟, 范志平. 盐掺杂聚苯胺的研究进展[J]. 现代化工, 2015, 35(12): 14-18,20.
[13] 邵春霞, 张丽华, 武娟, 张彬. 原位吸附聚合法制备聚苯胺/废弃丁羟黏合剂复合导电材料[J]. 现代化工, 2014, 34(5): 65-68.
[14] 王素敏,王奇观,森山広思. C60/聚苯胺自组装薄膜的制备及性能研究[J]. , 2010, 30(8): 0-0.
[15] 冉奋,王翎任,范雄峰,孔令斌,罗永春,康龙. 二次颗粒结构聚苯胺的制备及其超级电容性能[J]. , 2009, 29(9): 0-0.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-37
版权所有 © 《现代化工》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn