炭吸附La2O3/TiO2复合粉体的制备及其光催化性能研究
郝淳林, 王丽红, 郭贵宝
内蒙古科技大学化学与化工学院, 内蒙古 包头 014010
Preparation of La2O3/TiO2 nanocomposite powder by carbon adsorption and study on its photocatalytic properties
HAO Chun-lin, WANG Li-hong, GUO Gui-bao
School of Chemistry and Chemical Engineering, Inner Mongolia University of Science & Technology, Baotou 014010, China
下载:  PDF (2459KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 采用炭吸附共沉淀法制备了La2O3/TiO2催化剂,利用TG-DTG、XRD、TEM、UV-Vis等对催化剂进行表征,并考察了不同条件制备的La2O3/TiO2对可见光催化甲基橙降解效果的影响。结果表明,炭黑的加入可有效阻止粉体在制备、干燥及焙烧过程中的团聚和烧结;在600℃煅烧后得到的粉体结晶度高、颗粒分散均匀、颗粒粒径小。在可见光照射1 h后,炭吸附沉淀法制备的La2O3/TiO2对甲基橙的降解率高达92.25%,是普通沉淀法制得的La2O3/TiO2的3倍,光催化活性显著提高。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
郝淳林
王丽红
郭贵宝
关键词:  炭吸附  La2O3/TiO2  光催化  甲基橙    
Abstract: La2O3/TiO2 photocatalyst is prepared by carbon adsorption co-precipitation method.The samples are characterized by TG-DTG,XRD,TEM and UV-Vis.The impacts of La2O3/TiO2 prepared under different conditions on the degradation of methyl orange by using visible light irradiation are studied.Results show that the addition of carbon black during the reaction can effectively prevent the agglomeration and sintering of the particles during the preparation,drying and roasting processes.The powder obtained after calcination at 600℃ has high crystallinity,uniform particle dispersion,and small particle size.Under visible light irradiation for 1 h,the degradation rate of methyl orange over La2O3/TiO2 prepared by carbon adsorption co-precipitation method can reach as high as 92.25%,which is three times that over La2O3/TiO2 prepared by common precipitation method,representing a significantly improved photocatalytic activity.
Key words:  carbon adsorption    La2O3/TiO2    photocatalysis    methyl orange
收稿日期:  2020-02-03      修回日期:  2020-10-10          
ZTFLH:  O643  
基金资助: 国家自然科学基金(21463026)
通讯作者:  郭贵宝(1970-),男,博士,教授,研究方向为光催化降解,通讯联系人,ggb66733@sohu.com。    E-mail:  ggb66733@sohu.com
作者简介:  郝淳林(1993-),男,硕士研究生,研究方向为光催化降解,291179524@qq.com
引用本文:    
郝淳林, 王丽红, 郭贵宝. 炭吸附La2O3/TiO2复合粉体的制备及其光催化性能研究[J]. 现代化工, 2020, 40(12): 112-115.
HAO Chun-lin, WANG Li-hong, GUO Gui-bao. Preparation of La2O3/TiO2 nanocomposite powder by carbon adsorption and study on its photocatalytic properties. Modern Chemical Industry, 2020, 40(12): 112-115.
链接本文:  
https://www.xdhg.com.cn/CN/10.16606/j.cnki.issn0253-4320.2020.12.023  或          https://www.xdhg.com.cn/CN/Y2020/V40/I12/112
[1] Fox M A,Dulay M T.Heterogeneous photocatalysis[J].Chem Rev,1993,93(1):341-357.
[2] Li L,Yan J,Wang T,et al.Sub-10 nm rutile titanium dioxide nanoparticles for efficient visible-light-driven photocatalytic hydrogen production[J].Nat Commun,2015,6:5881-5891.
[3] Minabe T,Tryk D A,Sawunyama P,et al.TiO2-mediated photodegradation of liquid and solid organic compounds[J].J Photoch Photobio A,2000,137(1):53-62.
[4] Herrmann H J.Heterogeneous photocatalysis:Fundamentals and applications to the removal of various types of aqueous pollutants[J].Catal Today,1999,53(1):115-129.
[5] Linsebigler A L,Lu G,Yates J T.Photocatalysis on TiO2 surfaces:Principles,mechanisms,and selected results[J].Chem Rev,1995,95(3):735-758.
[6] Liu S,Yu J,Jaroniec M.Tunable photocatalytic selectivity of hollow TiO2 microspheres composed of anatase polyhedra with exposed {001} facets[J].J Am Chem Soc,2010,132:11914-11916.
[7] O″Regan B,GräTzel M.A low-cost,high-efficiency solar cell based on dye-sensitized colloidal TiO2 films[J].Nature,1991,353:737-740.
[8] Habisreutinger S N,Schmidt-Mende L,Stolarczyk J K.Photocatalytic reduction of CO2 on TiO2 and other semiconductors[J].Angew Chem Int Ed,2013,52(29):7372-7408.
[9] Ma Y,Wang X,Jia Y,et al.Titanium dioxide-based nanomaterials for photocatalytic fuel generations[J].Chem Rev,2014,114:9987-10043.
[10] Liu M,Qiu X,Miyauchi M,et al.Energy-level matching of Fe(Ⅲ) ions grafted at surface and doped in bulk for efficient visible-light photocatalysts[J].J Am Chem Soc,2013,135:10064-10072.
[11] Borgarello E,Kiwi J,Graetzel M,et al.Visible light induced water cleavage in colloidal solutions of chromium-doped titanium dioxide particles[J].J Am Chem Soc,1982,104:2996-3002.
[12] Chen X,Burda C.The electronic origin of the visible-light absorption properties of C-,N- and S-doped TiO2 nanomaterials[J].J Am Chem Soc,2008,130:5018-5019.
[13] Asahi R,Morikawa T,Ohwaki T,et al.Visible——light photocatalysis in nitrogen-doped titanium oxides[J].Science,2001,293:269-271.
[14] Sakthivel S,Kisch H.Daylight photocatalysis by carbon-modified titanium dioxide[J].Angew Chem Int Ed,2003,42:4908-4911.
[15] Xiao Y F,Liu S.Research progress on photocatalytic activity of silica-modified titanic oxide[J].Inorg Chem Industry,2007,39(9):5-9.
[16] Vinodgopal K,Bedja I,Kamat P V.Nanostructured semiconductor films for photocatalysis.photoelectrochemical behavior of SnO2/TiO2 composite systems and its role in photocatalytic degradation of a textile azo dye[J].Chem Mater,1996,8:2180-2187.
[17] Xu Anwu,Gao Y,Liu H Q.The preparation,characterization,and their photocatalytic activities of rare-earth-doped TiO2 nanoparticle[J].J Catal,2002,207(2):151-157.
[18] Song K Y,Park M K,Kwon Y T,et al.Preparation of transparent particulate MoO3/TiO2 and WO3/TiO2 films and their photocatalytic properties[J].Chem Mater,2001,13:2349-2355.
[19] Wang C,Shao C,Zhang X,et al.SnO2 Nanostructures-TiO2 nanofibers heterostructures:controlled fabrication and high photocatalytic properties[J].Inorg Chem,2009,48:7261-7268.
[20] Jiao Y C,Zhu M F,Chen F,et al.La-doped titania nanocrystals with superior photocatalytic activity prepared by hydrothermal method[J].Chin J Catal,2013,34(3):585-592.
[21] 康巧梅,洪臣熙.La2O3-TiO2的制备及其光催化性能[J].化工环保,2015,35(4):432-437.
[22] Yuan W J,Zhou Y M.Reasons for aggregation of nanoparticles and solutions[J].Mater Rev,2003,22(3):59-61.
[1] 赵丹, 梁飞雪, 封瑞江, 鞠佳. 不同形貌CeO2的制备及光催化性能研究[J]. 现代化工, 2020, 40(S1): 203-206.
[2] 黄建舒, 苏复, 刘志英, 徐炎华. Ag/AgBr/Bi2MoO6等离子体光催化剂的制备及其降解罗丹明B性能的研究[J]. 现代化工, 2020, 40(9): 89-95.
[3] 张根, 黄自力, 葛胜涛, 田亮, 张海军. Bi4Ti3O12/g-C3N4复合光催化剂的制备及其光催化性能研究[J]. 现代化工, 2020, 40(8): 83-87,92.
[4] 郭波, 李赛, 徐婷婷, 张磊. 膨胀珍珠岩负载纳米铁降解酸性大红与甲基橙的研究[J]. 现代化工, 2020, 40(8): 107-112.
[5] 宋月红, 代卫丽, 周春生, 赵杰, 赵敬哲. 组装态Bi5O7I纳米材料的制备及其光催化性能研究[J]. 现代化工, 2020, 40(7): 100-104.
[6] 张海楠, 左士祥, 刘文杰, 李霞章, 姚超. HNTs/TiO2/MoS2复合材料的制备及其在氯四环素光催化降解中的应用[J]. 现代化工, 2020, 40(7): 122-126,132.
[7] 刘书松, 金星龙. 复合光催化剂Bi5O7I/Ag3PO4的制备及其光催化性能研究[J]. 现代化工, 2020, 40(7): 127-132.
[8] 潘会, 胡轶, 胡帅帅. Fe、Ni掺杂ZnO纳米材料的光学、磁性及光催化性能的研究[J]. 现代化工, 2020, 40(7): 136-140.
[9] 张晶晶, 杨竹苇, 王林山, 晁雷. ZnO-BiOI复合催化剂的制备及其光催化降解联苯胺性能研究[J]. 现代化工, 2020, 40(6): 169-174.
[10] 时晓羽, 李会鹏, 赵华, 张杰. 硫掺杂高比表面积g-C3N4的制备及其光催化性能的研究[J]. 现代化工, 2020, 40(4): 167-172.
[11] 任秋燕, 傅敏, 汪成, 季雨晴. Bi2S3复合光催化材料可见光催化研究进展[J]. 现代化工, 2020, 40(3): 60-63.
[12] 岳琳, 张迎, 蒋永丰, 孙文会, 李再兴, 廉静, 罗晓. (NH4)3PW11O39Sn/TiO2复合材料光催化降解染料废水的研究[J]. 现代化工, 2020, 40(3): 152-156,161.
[13] 冉孟家, 谷晋川, 余乐. TiO2/锂硅粉-H2O2体系光催化降解邻苯二甲酸二甲酯机理分析[J]. 现代化工, 2020, 40(3): 167-171,175.
[14] 郭田辉, 张守臣. 多形貌二氧化钛/石墨烯复合材料的制备及光催化性能研究[J]. 现代化工, 2020, 40(3): 172-175.
[15] 刘雯雯, 柴涛, 兰树仁, 张新宇. 石墨烯-纳米二氧化钛复合材料的绿色制备及性能研究[J]. 现代化工, 2020, 40(3): 186-189.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-37
版权所有 © 《现代化工》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn