Abstract: KH560 is used as crosslinking agent to improve the fastness of La-Gd/ZnO nanorod arrays on the surface of cotton fabrics.La-Gd/ZnO nanorod arrays grow in-situ on the surface of cotton fabrics through low temperature hydrothermal method by using zinc nitrate and hexamethylene tetramine as raw materials,polyethylene glycol 2000 as morphology control agent and KH560 as crosslinking agent.The prepared samples are characterized by XRD,SEM,UV-siv and other measurements.The analysis results show that cotton fabric modified by 3% La-3% Gd/ZnO nanorod arrays performs excellent anti-ultraviolet and photocatalytic properties,and its anti ultraviolet index-UPF increases from 10.06 to 420.21 after modification.The degradation rate of methylene blue solution reaches 92.15% under irradiation of ultraviolet for 150 min with the presence of as-prepared catalyst,and that reaches 87.59% under irradiation of solar light for 8 h.After 10 times of washing by water,the photocatalytic performance of the prepared catalyst only decreases by 1.3% and its UPF remains unchanged,reflecting its good fastness.
顾益飞, 王黎明, 沈勇, 徐丽慧, 孙洁. La-Gd共掺ZnO纳米棒的性能及其应用研究[J]. 现代化工, 2018, 38(4): 139-143.
GU Yi-fei, WANG Li-ming, SHEN Yong, XU Li-hui, SUN Jie. Preparation of La-Gd/ZnO nanorods and study on its performance and application. Modern Chemical Industry, 2018, 38(4): 139-143.
[1] 张留成,蔡克峰.纳米氧化锌材料的最新研究和应用进展[J].材料导报,2006,(20):13-15. [2] 施利毅,马书蕊,欣冯.一维氧化锌纳米棒制备技术的最新研究进展[J].材料导报,2006,(20):86-89. [3] 姜聚慧,王林浩,张圣麟,等.铋和镧共掺杂二氧化钛半导体的制备与光催化性能研究[J].水处理技术,2011,37(12):32-35. [4] Yi G C,Wang C R,Park W I.ZnO nanorods:Synthesis,characterization and applications[J].Semiconductor Science and Technology,2005,20(4):22-34. [5] Law M,Goldberger J,Yang P D.Semiconductor nanowires and nanotubes[J].Annual Review of Materials Research,2004,34(1):83-88. [6] 任坤,黄晶,贺小燕,等.热喷涂制备TiO2光催化涂层研究进展[J].表面技术,2015,44(4):66-83. [7] Tong Y H,Liu Y C,Dong L,et al.Growth of ZnO nanostructures with different morphologies by using hydrothermal technique[J].Journal of Physical Chemistry B,2006,110(41):20263-20267. [8] Yamabi S,Imai H.Growth conditions for wurtzite zinc oxide films in aqueous solutions[J].Journal of Materials Chemistry,2002,12(12):3773-3778. [9] Chen Z T,Gao L.A facile route to ZnO nanorod arrays using wet chemical method[J].Journal of Crystal Growth,2006,293(2):522-527. [10] Guo M,Diao P,Wang X D,et al.The effect of hydrothermal growth temperature on preparation and photoelectrochemical performance of ZnO nanorod array films[J].Journal of Solid State Chemistry,2005,178(10):3210-3215. [11] Ma T,Guo M,Zhang M,et al.Density-controlled hydrothermal growth of well-aligned ZnO nanorod arrays[J].Nanotechnology,2007,18(3):4024-4027. [12] 魏志钢,潘湛昌,徐阁,等.Gd掺杂锐钛矿型二氧化钛的第一性原理研究[J].材料科学与工程学报,2011,29(2):217-220. [13] Armelao L,Bottaro G,Pascolini M,et al.Structure-luminescence correlations in europium-doped sol-gel ZnO nanopowders[J].Journal of Physical Chemistry C,2008,112:4049-4054. [14] Islam M N,Ghosh T B,Chopra K L,et al.XPS and X-ray diffraction studies of aluminum-doped zinc oxide transparent conducting films[J].Thin Solid Films,1996,280:20-25. [15] Major S,Kumar S,Bhatnagar M,et al.Effect of hydrogen plasma treatment on transparent conducting oxides[J].Applied Physics Letter,1986,49:394-396. [16] Wang Y,Sun L,Kong L G,et al.Room-temperature ferro-magnetism in co-doped ZnO bulk induced by hydrogenation[C]//E.Talik.Multi-component Alloys and Intermetallic Compounds for Magnetic Applications and Nanotechnology.Poland:Journal of Alloys and Compounds,2006,423:256-259. [17] Zhang L,Han M D,Tan O K,et al.Facile fabrication of Ag/C-TiO2 nanoparticles with enhanced visible light photocatalytic activity for disinfection of Escherichia coli and Enterococcus faecalis[J].J Mater Chem B,2013,1(4):564-570.