现代化工  2019, Vol. 39 Issue (6): 178-181,183    DOI: 10.16606/j.cnki.issn0253-4320.2019.06.037
  科研与开发 本期目录 | 过刊浏览 | 高级检索 |
氧化铝制备工艺对银催化剂性能的影响
林伟
中国石化北京化工研究院燕山分院, 北京 102500
Effect of alumina preparation process on performances of silver catalyst
LIN Wei
Yanshan branch of SINOPEC Beijing Research Institute of Chemical Industry, Beijing 102500, China
下载:  PDF (10325KB) 
输出:  BibTeX | EndNote (RIS)      
摘要 研究了不同类型氧化铝晶体形貌与制备工艺对银催化剂及其载体性能的影响。结果表明,经高温焙烧后,氧化铝晶粒虽然已经有长大的趋势,但未完全发育,仍存在很多"蠕虫状"无规则氧化铝晶粒;其中,添加硼化物载体的晶粒长得相对更完整一些,对块状氧化铝的生成较为有利;添加胺基化合物有利于水合氧化铝向α-氧化铝的转变,但其实际效果稍低于硼化物。采用比表面积较高的氧化铝作为载体,制得的银催化剂的反应活性较高。若通过添加造孔剂形成较大气孔,催化剂的选择性得到明显提高。
服务
把本文推荐给朋友
加入引用管理器
E-mail Alert
RSS
作者相关文章
林伟
关键词:  氧化铝  晶体形貌  造孔剂  银催化剂  环氧乙烷    
Abstract: The effects of different types of alumina crystal morphology and preparation process on the performances of silver catalyst and its support were studied.The results indicated that the alumina grains had a tendency to grow after calcinations at high temperature,but it was not fully developed,and there were still many "worm-like" irregular alumina grains.Meanwhile,the alumina grain with addition of boride was relatively more complete,which was more favorable for the formation of bulk alumina.Amine compound was beneficial to the conversion of hydrated alumina to α-alumina,but its actual effect was slightly lower than that of boride.The silver catalyst prepared by the carrier with a high specific surface area had high activity.If a large pore of carrier was formed by adding a pore former,the selectivity of the catalyst was remarkably improved.
Key words:  alumina    crystal morphology    pore former    silver catalyst    ethylene oxide
收稿日期:  2019-02-15      修回日期:  2019-04-04          
ZTFLH:  TQ426  
通讯作者:  林伟(1977-),男,博士,高级工程师,研究方向为环氧乙烷银催化剂的研制,通讯联系人,linwei.bjhy@sinopec.com。    E-mail:  linwei.bjhy@sinopec.com
引用本文:    
林伟. 氧化铝制备工艺对银催化剂性能的影响[J]. 现代化工, 2019, 39(6): 178-181,183.
LIN Wei. Effect of alumina preparation process on performances of silver catalyst. Modern Chemical Industry, 2019, 39(6): 178-181,183.
链接本文:  
http://www.xdhg.com.cn/CN/10.16606/j.cnki.issn0253-4320.2019.06.037  或          http://www.xdhg.com.cn/CN/Y2019/V39/I6/178
[1] 戴厚良,姚虎卿,欧阳平凯.环氧乙烷/乙二醇生产技术现状及发展建议[J].现代化工,2005,25(12):11-15.
[2] 杨忠兵.环氧乙烷产业技术现状与展望[J].石油化工技术与经济,2014,30(6):52-56.
[3] 孙果宋,李华锋,王俊,等.环氧乙烷深加工产品生产技术进展[J].精细化工,2010,27(10):937-941.
[4] 赵楠楠.环氧乙烷生产技术进展及产能现状[J].化工时刊,2015,29(5):23-26.
[5] 崔小明.环氧乙烷生产技术进展及市场分析[J].精细与专用化学品,2014,22(5):12-18.
[6] 刘宗语.环氧乙烷/乙二醇生产技术进展[J].化工进展,2013,32(6):1214-1218.
[7] Suljo Linic,Mark A Barteau.Formation of a stable surface oxametallacycle that produces rthylene oxide[J].J Am Chem Soc,2002,124(2),310-317.
[8] Podgornov E A,Prosvirin I P,Bukhtiyarov V I.XPS,TPD and TPR studies of Cs-O complexes on silver:Their role in ethylene epoxidation[J].Journal of Molecular Catalysis A:Chemical,2000,158(1):337-343.
[9] Stegelmann C,Schiødt N C,Campbell C T,et al.Microkinetic modeling of ethylene oxidation over silver[J].Journal of Catalysis,2004,221(2):630-649.
[10] Piao H,Enever M C N,Adib K,et al.High resolution X-ray photoelectron spectroscopy of styrene oxide adsorption and reaction on Ag(111)[J].Surface Science,2004,571(1-3):139-145.
[11] Siriphong Rojluechai,Sumaeth Chavadej,Johannes W Schwank,et al.Activity of ethylene epoxidation over high surface area alumina support Au-Ag catalysts[J].Journal of Chemical Engineering of Japan,2006,39(3):321-326.
[12] Enever M,Linic S,Uffalussy K,et al.Synthesis,structure,and reactions of stable oxametallacycles from styrene oxide on Ag(111)[J].J Phys Chem B,2005,109(6):2227-2233.
[13] Suljo Linic,Mark A Barteau.Control of ethylene epoxidation selectivity by surface oxametallacycles[J].Journal of the American Chemical Society,2003,125(14):4034-4035.
[14] Lauritzen,Ann M.Ethylene oxide catalyst and process for preparing the catalyst:US,4761394[P].1988-08-02.
[15] Lauritzen,Ann M.Ethylene oxide catalyst and process for preparing the catalyst:US,4766105[P].1988-08-23.
[16] 周允红,周晓龙,曹建春,等.负载银催化剂的制备与应用的研究进展[J].石油化工,2014,43(6):721-728.
[17] Nabil Rizkalla,Andrzej Rokicki.Carrier treatment to improve catalytic performance of an ethylene oxide catalyst:US,2017/0369460A1[P].2017-12-28.
[18] Dellamorte J C,Lauterbach J,Barteau M A.Promoter-induced morphological changes of Ag catalysts for ethylene epoxidation[J].Ind Eng Chem Res,2009,48(13):5943-5953.
[19] 皇环环,王倩,吴丽,等.低温燃烧合成法制备的氧化铝陶瓷粉体的发光特性[J].光谱学与光谱分析,2018,38(9):2676-2680.
[20] 刘峰,何德东,陆继长,等.尿素研磨燃烧法合成Ce0.8Zr0.2O2固溶体对乙硫醇催化分解的研究[J].中国稀土学报,2018,36(1):53-60.
[1] 陈新华, 马永梅. 氢氧化钠刻蚀多孔阳极氧化铝制备氧化铝纳米柱及其疏水性能[J]. 现代化工, 2019, 39(2): 121-124,126.
[2] 刘婷婷, 乔建江. 复合氢氧化铝-季戊四醇的制备及其应用研究[J]. 现代化工, 2018, 38(9): 155-159.
[3] 郑峰伟, 孙成, 陈富金, 李国斌, 苏毅. 粉煤灰中氧化铝提取的研究进展[J]. 现代化工, 2018, 38(3): 37-41.
[4] 王梦凡, 隋贤栋, 黄肖容. 氧化铝蜂窝陶瓷超滤膜的制备及表征[J]. 现代化工, 2017, 37(12): 126-129.
[5] 金伟, 田永胜, 查乐林, 徐乾, 曾丹林, 崔佳伟, 王光辉. F127对MoO3/Al2O3结构及其催化氧化脱除苯并噻吩性能的影响[J]. 现代化工, 2017, 37(11): 75-79.
[6] 宋文娟, 王燕, 赵会晶, 高中飞, 王明贺, 郭登峰. 烷氧基化法一步合成乙二醇甲醚苯甲酸酯的研究[J]. 现代化工, 2016, 36(12): 90-93.
[7] 郭立颖, 高学, 马秀云, 史君, 贺俊海. 负载硅离子液体的合成及其催化性能[J]. 现代化工, 2016, 36(1): 90-92,94.
[8] 马钊, 王传琴, 李广学, 段艳文, 彭飞. 从粉煤灰中提取氧化铝的研究现状[J]. 现代化工, 2015, 35(3): 34-36,38.
[9] 惠坤龙, 张君涛, 申志兵. 介孔氧化铝的合成及应用进展[J]. 现代化工, 2015, 35(3): 50-54.
[10] 刘亚青, 刘玉敏, 胡永琪. 激光粒度仪测定近纳米氢氧化铝粒径的研究[J]. 现代化工, 2015, 35(3): 175-177.
[11] 董飞, 秦金平, 陈名浪, 高记. 混合纳米级Al2O3/S PLOT毛细管色谱柱的研制及应用[J]. 现代化工, 2014, 34(7): 159-162.
[12] 丁巍, 王鼎聪, 赵德智, 柯明. 纳米自组装催化剂金属分散度对催化活性的影响[J]. 现代化工, 2014, 34(5): 113-116.
[13] 丁云飞, 伍彬, 吴会军. 基于模板热压法制备超疏水柱状结构表面[J]. 现代化工, 2014, 34(11): 65-68.
[14] 周润欣, 李思洋, 田野, 王鼎聪, 赵德智, 宋官龙. Mo-Ni纳米自组装催化剂的表征与活性评价[J]. 现代化工, 2014, 34(11): 69-72.
[15] 陶中东, 朱科泾, 吴东方, 黄凯. 催化氧化处理高浓度印染废水的催化剂研究[J]. 现代化工, 2014, 34(10): 91-93.
No Suggested Reading articles found!
Viewed
Full text


Abstract

Cited

  Shared   
  Discussed   
京ICP备09035943号-37
版权所有 © 《现代化工》编辑部
本系统由北京玛格泰克科技发展有限公司设计开发 技术支持:support@magtech.com.cn